Celcon® MC90
乙缩醛（POM）共聚物
Ticona
产品说明
Celcon® acetal copolymer grade MC90 is a mineral reinforced grade offering low warp, improved dimensional stability, improved stiffness, improved practical impact and retention of other base resin properties with good moldability.
Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GNR, 03-002, M
总体
材料状态 • 已商用：当前有效
供货地区 • 北美洲 • 拉丁美洲 • 南美洲
填料/增强材料 • 矿物填料
性能特点 • 尺寸稳定性良好 • 刚性，良好 • 抗撞击性，良好
• 低翘曲性 • 共聚物 • 良好的成型性能
RoHS 合规性 • 联系制造商
形式 • 颗粒料
加工方法 • 注射成型
多点数据 • Isothermal Stress vs. Strain (ISO 11403-1)
树脂ID (ISO 1043) • POM
物理性能
比重
收缩率
流动
横向流动
横向流量
流量
吸水率 饱和, 23°C
平衡, 23°C, 50% RH
机械性能
拉伸模量
抗张强度 屈服, 23°C
屈服
拉伸应变 (屈服)
弯曲模量
23°C
23°C
冲击性能
简支梁缺口冲击强度
-30°C 23°C
悬壁梁缺口冲击强度
23°C
23°C
热性能
热变形温度
0.45 MPa, 未退火
1.8 MPa, 未退火
1.8 MPa, 未退火
维卡软化温度
熔融温度 2
额定值单位制 测试方法
1.48g/cm³ ASTM D792
ISO 1183
1.9% ASTM D955
1.6% ASTM D955
1.6% ISO 294-4
1.9% ISO 294-4
ISO 62
0.75%
0.20%
额定值单位制 测试方法
3000MPa ISO 527-2/1A/1
53.1MPa ASTM D638
57.0MPa ISO 527-2/1A/50
8.0% ISO 527-2/1A/50
2960MPa ASTM D790
2850MPa ISO 178
额定值单位制 测试方法
ISO 179/1eA
5.5kJ/m²
6.8kJ/m²
64J/m ASTM D256
6.3kJ/m² ISO 180/1A
额定值单位制 测试方法
152°C ISO 75-2/B
93.3°C ASTM D648
97.0°C ISO 75-2/A
161°C ISO 306/B50
165°C ISO 11357-3
ASTM D3418
1 / 2
Celcon® MC90 2012年10月14日
乙缩醛（POM）共聚物
Ticona
热性能 额定值单位制 测试方法
线形膨胀系数 ISO 11359-2
流动 0.00010cm/cm/°C
横向 0.00012cm/cm/°C
补充信息 额定值单位制 测试方法
ISO Type POM-K, M-GNR, 03-002, M ISO 9988-1
注射 额定值单位制
加工（熔体）温度 182 到 199°C
模具温度 82.0 到 93.0°C
注射说明
Standard reciprocating screw injection molding machines with a high compression screw (minimum 3:1 and preferably 4:1) and low back pressure (0.35 Mpa/50 PSI) are favored. Using a low compression screw (I.E. general purpose 2:1 compression ratio) can result in unmelted particles and poor melt homogeneity. Using a high back pressure to make up for a low compression ratio may lead to excessive shear heating and deterioration of the material.
Melt Temperature: Preferred range 182-199 C (360-390 F). Melt temperature should never exceed 230 C (450 F).
Mold Surface Temperature: Preferred range 82-93 C (180-200 F) especially with wall thickness less than 1.5 mm (0.060 in.). May require mold temperature as high as 120 C (250 F) to reproduce mold surface or to assure minimal molded in stress. Wall thickness greater than 3mm (1/8 in.) may use a cooler (65 C/150 F) mold surface temperature and wall thickness over 6mm (1/4 in.) may use a cold mold surface down to 25 C (80 F). In general, mold surface temperatures lower than 82 C (180 F) may hinder weld line formation and produce a hazy surface or a surface with flow lines, pits and other included defects that can hinder part performance.