Celcon® M140-L1
乙缩醛（POM）共聚物
Ticona

产品说明

Celcon® M140-L1 is a general purpose acetal copolymer material with a slightly lower viscosity for improved flow in molding that has been modified to reduce or eliminate noise (squeak) when wearing against itself.

总体

材料状态 • 已商用：当前有效  
供货地区 • 北美洲 • 拉丁美洲 • 南美洲
性能特点 • 共聚物 • 良好的流动性 • 一般目的
用途 • 一般目的  
RoHS 合规性 • 联系制造商  
形式 • 颗粒料  
加工方法 • 注射成型  
多点数据 • Isothermal Stress vs. Strain (ISO 11403-1) 

物理性能 额定值单位制 测试方法
密度 1.40g/cm³ ISO 1183
溶化体积流率（MVR） (190°C/2.16 kg) 12.0cm³/10min ISO 1133
收缩率  ISO 294-4
横向流量 1.7% 
流量 1.9% 
机械性能 额定值单位制 测试方法
拉伸模量 2600MPa ISO 527-2/1A/1
拉伸应力 (屈服) 63.0MPa ISO 527-2/1A/50
拉伸应变 (屈服) 9.5% ISO 527-2/1A/50
弯曲模量 (23°C) 2500MPa ISO 178
冲击性能 额定值单位制 测试方法
简支梁缺口冲击强度 (23°C) 6.0kJ/m² ISO 179/1eA
悬壁梁缺口冲击强度 (23°C) 5.7kJ/m² ISO 180/1A
热性能 额定值单位制 测试方法
热变形温度 (1.8 MPa, 未退火) 100°C ISO 75-2/A
维卡软化温度 161°C ISO 306/B50
熔融温度 2 166°C ISO 11357-3
线形膨胀系数  ISO 11359-2
流动 0.00011cm/cm/°C 
横向 0.00012cm/cm/°C 
充模分析 额定值单位制 测试方法
熔体密度 1.17g/cm³ Internal Method
  
注射 额定值单位制 
加工（熔体）温度 182 到 199°C 
模具温度 82.0 到 93.0°C 
注射说明  

Standard reciprocating screw injection molding machines with a high compression screw (minimum 3:1 and preferably 4:1) and low back pressure (0.35 Mpa/50 PSI) are favored. Using a low compression screw (I.E. general purpose 2:1 compression ratio) can result in unmelted particles and poor melt homogeneity. Using a high back pressure to make up for a low compression ratio may lead to excessive shear heating and deterioration of the material.

Melt Temperature: Preferred range 182-199 C (360-390 F). Melt temperature should never exceed 230 C (450 F).

Mold Surface Temperature: Preferred range 82-93 C (180-200 F) especially with wall thickness less than 1.5 mm (0.060 in.). May require mold temperature as high as 120 C (250 F) to reproduce mold surface or to assure minimal molded in stress. Wall thickness greater than 3mm (1/8 in.) may use a cooler (65 C/150 F) mold surface temperature and wall thickness over 6mm (1/4 in.) may use a cold mold surface down to 25 C (80 F). In general, mold surface temperatures lower than 82 C (180 F) may hinder weld line formation and produce a hazy surface or a surface with flow lines, pits and other included defects that can hinder part performance.

1 / 2

 
 
 
 
 
 
Celcon® M140-L1 2012年10月14日
乙缩醛（POM）共聚物
Ticona
备注
1 一般属性：这些不能被视为规格。

2 10°C/min